ELECTROPLATING The problem was to discover which electrolyte is the best. An electrolyte is a liquid you electroplate in. Water, vinegar, and vinegar with salt stirred in it were the three electrolytes used. Which is the best electrolyte for copperplating a nickel Is there a difference between these electrolytes or are they all the same Electroplating is the process of coating with metal by means of electric current. When electroplating is really used it is more complicated than the process used in this experiment. In a real plating tank the cathode, or metal to be plated, is negatively charged.
The anode, or plating metal, is charged positively. Then some of the atoms on the anode come off with the electric current and on to the cathode. The cathodes old atoms are taken off with the electric current, leaving room for the anodes atoms (Ammen 38-39).
Electroplating is used to keep an old metal looking new. It can also be used to make one metal look like another. Electroplating is used in a lot of cases.
A very well known use is on cars. This keeps a car looking shiny and attractive. Copperplating is most commonly used to prevent metal from hardening. Silver plating is mainly used on tableware and electric contacts. Gold plating may be found on jewelry and watch cases. Zinc is often used to prevent corrosion of steel objects.
A nickel or chromium plating may be found on cars or household appliances (Electroplating).
Some coating procedures may have begun in early times. Modern electroplating did not start until the early 1800 s. After the invention of the battery at this time period, large amounts of current electricity became available. It also could deposit lead, copper, and silver. With the discovery of cyanide solution, deposits of gold, silver, copper and brass could be directly deposited on steel or iron.
The Essay on Nickel Metal Hydride Battery For Electric Vehicles
Electric vehicles can benefit us in many ways. Comparing with the internal combustion engine, EVs don't cause pollution when operating. They can run in a long period of time. Economically, because these vehicles using battery, they reduce the oil import and the imbalance trading in the US and also the users save a lot of money. The cells used for these vehicles are called Nickel metal hydride ...
This increased the commercial use of electroplating. The electroplating industry has grow and has developed many requirements in the electroplating process. Some commonly used metals today are iron, brass, silver, copper, cobalt, zinc, gold, lead, and chromium. Chromium is a very useful metal in this industry.
Chromium is very bright and stays this way for a very long time. Automobiles are the main items electroplated with this metal. That is what keeps a car bright. Hard-chromium is used to improve wear resistance of machine parts (Barrow).
My hypothesis was that vinegar and salt would work the best for copperplating a nickel since it is the densest electrolyte of the three. When this liquid is used more copper will come off the penny at a time. The process also goes the fastest in this solution. I thought that the water would go the slowest and would not work as well. This is because it is least dense of the three electrolytes. One 6-volt battery was needed to hook up to the coins.
Three nickels and three pennies are needed as the cathode and anode. Vinegar, water, and vinegar with salt mixed in it were used as the three electrolytes. Two different colored wires were needed to hook the coins to the battery. The nickel, or cathode, was hooked up to the negative part of the battery.
The penny, or anode, was hooked to the positive end. When they connected they were put in to the water filled jar. Then they were put in the vinegar and after that in the vinegar with salt in it (Gibson 177-179).
All three electrolytes gave different results. In water, the nickel did not appear to be plated at all, but there were bubbles surrounding both of the metals. In vinegar, the process was not as quick as in the vinegar with salt, but it electroplated perfectly fine.
In the vinegar mixed with salt, the results were great. It took only a couple of minutes for the nickel to be plated. The finished product was well coated. I also found out if you keep the coins in there for too long the penny becomes corroded and the nickel is totally plated. In conclusion, when an electrolyte is more dense it is better for electroplating.
The Term Paper on Electrolytes
Electrolytes are liquids that conduct electricity. Most need to be dissolved into water or another solvent. Battery¡¦s have an electrolyte in them, either as a liquid or as a paste. Liquid electrolytes are used in electrolysis, electroplating, and other chemical processes. When electrolytes dissolve they release positive and negative ions. The released ions carry electric charges between ...
Ammen, C. W. Electroplates handbook. PA: Tab Books, 1986. Barrow, Edward Regulated power for electrochemistry.
Electronics Now. Dec 1995: 29-36 Collier, P. F. Electroplating Colliers Encyclopedia. NY 1994 Gibson, Gary.
Science for Fun Experiments. Connecticut Copper Beach Books, 1996.